Aquathene APF-405-Self-adhesive modified bitumen waterproof membrane
PRODUCT DESCRIPTION
Aquathene APF-405 Self-adhesive modified bitumen waterproof membrane utilized aluminized Mylar film as surface reinforcing material, covered with asphalt adhesive material which contains active agent rubber . APF-405 can be used directly with polymer cement mortar in the construction (wet applied method), but also can be used according to the traditional construction method (dry applied ), so as to meet the different needs of projects. This product is especially suitable for the continuous construction of waterproof engineering design, when the construction period is long , and the exposure time of the membrane also is long, the component of APF-405 can function to reduce fold and the drum phenomenon of the materials.
WHERE TO USE
- Roofing, underground waterproof engineering
- The concealed waterproof project with a protective covering.
Applications: Indonesia Fantasy Island Project、Kenya Naima Railway Project
Strong stick relay good tensile strength, excellent waterproof performance, high reflectivity of sunshine, can prolong the service life of coiled material, and can reduce the indoor temperature of the building.
| Product name | Class | Membrane thickness |
|---|---|---|
| Aquathene APF-405 self-adhesive Modified bitumen waterproof Membrane | Type I, Type II | 1.2mm,1.5mm,2.0mm |
|
Item
|
Index
|
||
|---|---|---|---|
|
PET
|
|||
|
I
|
II
|
||
|
Expansion rate
|
Tension/(N/50mm) ≥
|
150
|
200
|
|
Elongation at maximum tension /% ≥
|
30
|
||
|
Elongation at break /% ≥
|
150
|
||
|
Nail shank tear strength /N ≥
|
30
|
40
|
|
|
Heat resistance
|
sliding / flowing less than 2mm
|
||
|
Low temperature flexibility /℃
|
-20
|
-30
|
|
|
Peeling strength /(N/mm)≥
|
Membrane V.S. Membrane
|
1.0
|
|
|
Membrane V.S. Aluminum board
|
1.5
|
||
|
Nail shank watertight
|
Pass
|
||
|
Expansion rate
|
Tension/(N/50mm) ≥
|
150
|
200
|
|
Elongation at maximum tension /% ≥
|
30
|
150
|
|
|
Tear strength /N ≥
|
12
|
25
|
|
|
Heat resistance
|
70℃，2h no sliding、flowing、dripping less
|
||
|
Low temperature flexibility /℃
|
-15℃ no crack
|
15℃ no crack
|
|