Aquaflex KS-100X-KS-100X Spider silk Bionic fiber waterproof mortar
PRODUCT DESCRIPTION
A new type of composite waterproof material developed by the technology of strengthening the cohesive force of high-strength fiber. The product is specially added with anti-cracking fiber, which can effectively enhance the comprehensive and anti-folding force of the coating, and can directly paste the tile.
Spider silk" design concept: the product adds fiber reinforced materials, so that the product has strong adhesion; in the product of the extramural and comprehensive test, the product is broken by pressure, and the fiber material in the product plays a bonding role. The effect is similar to that of spider silk. As one of the selling points of this product, filamentous fiber can represent the characteristics of the product more, so it is named as spider silk.
WHERE TO USE
Waterproof and anti-penetration of exterior walls and interior walls of buildings.
Waterproof and impervious to the water surface and back surface of underground works.
Waterproof and moisture proof for indoor kitchen and bathroom, balcony and floor.
Waterproof and anti-penetration of fire pools, landscape pools, canals and dams.
1.Add high-strength anti-cracking fiber
Strong cohesion
- Flexural, compressive and impact resistant crushing
- Prevent tiles from falling off
- Enhanced service life
2. Stronger adhesion
- Using high-strength fiberization cohesion technology, adding anti-cracking fiber can effectively enhance cohesion.
- The product has stronger adhesion, and the coating film is self-contained after it is dried, which makes the tile bond stronger.
3. Product strength rises fast
- The product strength rises fast, making the waterproof coating stronger, effectively preventing the brick removal phenomenon caused by the falling off of the waterproof layer.
34kg/set (liquid material + powder = 9kg + 25kg)
When the coating film thickness is 1mm, the usage is 1.5~2kg/m2 (the actual amount depends on the actual condition of the base surface and the required thickness of the waterproof layer.)
|
Item |
Index |
|
|
Setting time |
The initial setting |
≥45min |
|
≤24h |
||
|
The final setting |
||
|
0.6 |
||
|
|
Coating（7d）≥ |
|
|
Compressive strength/ MPa ≥ |
||
|
24 |
||
|
Flexural strength/MPa ≥ 7d |
||
|
1.0 |
||
|
Adhesive strength/MPa ≥ 28d |
||
|
1.2 |
||
|
No cracking or peeling |
||
|
Alkali resistance ≤ |
||
|
No cracking or peeling |
||
|
Heat resistance ≤ |
||
|
No cracking or peeling |
||
|
Frost resistance ≤ |
||
|
Shrinkage /% ≤ |
||
|
0.15 |
||
|
Water collection rate /% ≤ |
||
|
4.0 |
||