AQUACOAT KS-60-KS-60 SINGLE-COMPONENT HAND-APPLIED POLYUREA COATING
PRODUCT DESCRIPTION
Single-component hand-apply polyurea coating has high mechanical properties and elasticity, a modulus that matches that of concrete, and good weather resistance. After it is cured, the film still has an elongation of at least 100% or more under long-term freezing conditions at -45 ° C.
WHERE TO USE
It is mainly used for exposed waterproof, protective, anti-corrosive functional elastic coatings, especially for high-deformation nodes with waterproof and stress-concentrated detail node areas. Used in long-lasting waterproofing projects.
Exposed elastic waterproof coating for house construction.
Waterproofing of various concrete detail node areas.
Elastic coating for anti-seepage of various joints such as hydraulic joints and cracks.
Exposed waterproof and wear-resistant elastic coating for traffic bridges, flyovers, and air passages.
Metal structure roofing with elastic coating for waterproofing.
Waterproof of various pools.
Use of various cement mortar liquid cement.
Elastic coatings for other kinds of waterproof, anti-corrosion, wear-resistant floor, protection and other uses.
- Single component, curing with the moisture of the air, easy to construct;
- The coating is compact without joint;
- The one time construction thickness can be 0.5-1.0mm and not easy to flow in vertical construction;
- Good water resistance, good wear resistance and excellent elasticity;
- Good weather resistance and corrosion resistance;
- Do not content heavy metal, green and environmental protection;
- The coating serve for a long time in the temperature range of - 35 ° C ~ 80 ° C.
5kg/pail, 20kg/pail
No. |
ITEM |
REQUIREMENT |
TYPICAL VALUE |
1 |
Component |
One-component |
One-component |
2 |
Density,g/ml |
1.0±0.1 |
1.10 |
3 |
Surface drying time ,TFT,h |
<1.5 |
0.8 |
4 |
Fully drying time ,h |
<12 |
8 |
5 |
Tensile Strength,Mpa |
>15 |
18.6 |
6 |
Elongation at break,% |
300 |
375 |
7 |
Low temperature -45 ℃ elongation,% |
>100) |
150 |
8 |
Tear strength,N/mm |
40 |
61 |
9 |
Drawing adhesive strength (with primer),MPa |
2.5 |
4.8 |
10 |
Peel adhesive strength (with primer),N/mm |
2 |
3.2 |
11 |
Peel strength after immersion in high and low temperatures,N/mm |
1.5 |
2 |
12 |
80 ℃ heat treatment,168h |
good |
good |
13 |
2% sulfuric acid treatment (soak for 168h) |
good |
good |
14 |
2% sodium hydroxide treatment (soak for 168h) |
good |
good |
15 |
3% sodium chloride treatment (soak for 168h) |
good |
good |
16 |
No. 0 diesel (168h soak) |
good |
good |
17 |
Artificial weathering(QUVA2000h) |
Does not crack |
Does not crack |
18 |
Thermal emissivity |
0.80 |
0.85 |
19 |
Light reflectivity |
0.82 |
0.83 |