Aquaprufe PVC-Waterproof membrane
PRODUCT DESCRIPTION
Aquaprufe PVC (Polyvinyl chloride) Waterproof membrane is a type of high polymer waterproof material of high performance. It uses polyvinyl chloride as raw material, adding specified additives and anti-aging agents, prepared by advanced technique and equipment. The product has excellent tensile strength, strong elongation, small shrinkage rate, good flexibility at low temperature and long operating life.
WHERE TO USE
The Waterproof and damp proof construction of Industrial and civic roof, underground, water conservancy, railway, traffic construction as well as grain depot, swimming pool and water tank.
PRODUCT STRUCTURE
PRODUCT FEATURES
- Excellent tensile strength, elongation rate and dimensional stability after heat treatment.
- Great flexibility at low temperature and weather resistance.
- High compression resistant strength.
- Simple construction. Do the lap seam by heat welding operation.
- Remarkable anti-corrosion ability make it possible to apply to the special site
- Good plasticity make it easy to operate the details.
SPECIFICATION
|
Product name
|
model
|
Thickness(mm)
|
Width(m)
|
Length(m)
|
|---|---|---|---|---|
|
PVC waterproof membrane
|
Homogeneous (H) (Non-exposed)
|
1.2,1.5,2.0
|
2.0
|
20
|
|
Homogeneous (H) (Exposed)
|
||||
|
With fiber backing L (Non-exposed)
|
||||
|
With fiber backing L（Exposed）
|
||||
|
In-fabric reinforcement P（Exposed）
|
DATABASE
|
Item
|
Indes
|
|||
|---|---|---|---|---|
|
H
|
L
|
P
|
||
|
Thickness above scrim
|
-
|
-
|
-
|
|
|
Tensile performance
|
Max.tensile strength,(n/cm)≥
|
-
|
-
|
250
|
|
Tensile strength,mpa≥
|
10
|
120
|
-
|
|
|
Elongation at max. Tensile strength.%≥
|
-
|
-
|
15
|
|
|
Elongation at break,%≥
|
200
|
150
|
-
|
|
|
Dimensional chang after heat treatment
|
2.0
|
1.0
|
0.5
|
|
|
Flexibility at low temperature
|
-2.5℃，no cracking
|
|||
|
Water tightness
|
0.3mpa,2h,water tight
|
|||
|
Puncture resistance
|
0.5kg·m,imperneable
|
|||
|
Hydrostatic resistance(a)
|
-
|
-
|
20kg,impermeable
|
|
|
Lap seam peeling strength
|
4.0 or membrane breakage
|
3.0
|
||
|
Right-angled tear strength
|
50
|
-
|
-
|
|
|
Trapezoid tear strength
|
-
|
150
|
250
|
|
|
Water absorption(70℃,168h),%
|
After immersion≤
|
4.0
|
||
|
After drying≤
|
-4.0
|
|||
|
Heat aging(80℃)
|
Period,h
|
672
|
||
|
Appearance
|
No bubbling,crack,layered,bonding and hole
|
|||
|
Retention rate at max. Tension,%≥
|
-
|
85
|
85
|
|
|
Retention rate at max Tensile strength,%≥
|
85
|
-
|
-
|
|
|
Elongation retention rate at max tension,%≥
|
-
|
-
|
80
|
|
|
Elongation retention rate at break,%≥
|
80
|
80
|
-
|
|
|
Flexibility at low temperature
|
-20℃，no cracking
|
|||
|
Chemical resistance
|
Appearance
|
No bubbling,crack,layered,bonding and hole
|
||
|
Retention rate at max. Tension,%≥
|
-
|
85
|
85
|
|
|
Retention rate at max Tensile strength,%≥
|
85
|
-
|
-
|
|
|
Elongation retention rate at max tension,%≥
|
-
|
-
|
80
|
|
|
Elongation retention rate at break,%≥
|
80
|
80
|
-
|
|
|
Flexibility at low temperature
|
-20℃，no cracking
|
|||
|
Artificial weathering aging(c)
|
Period,h
|
1500(b)
|
||
|
Appearance
|
No bubbling,crack,layered,bonding and hole
|
|||
|
Retention rate at max. Tension,%≥
|
-
|
85
|
85
|
|
|
Retention rate at max Tensile strength,%≥
|
85
|
-
|
-
|
|
|
Elongation retention rate at max tension,%≥
|
-
|
-
|
80
|
|
|
Elongation retention rate at break,%≥
|
80
|
80
|
-
|
|
|
Flexibility at low temperature
|
-20℃，no cracking
|
|||